合金鋼襯板主要用于水泥廠、選礦、火電廠以及立磨、自磨機(jī)等,合金鋼襯板在使用過程中耐磨性好,不變形,不破碎,可以提高磨機(jī)生產(chǎn)力,減少磨機(jī)停機(jī)時(shí)間,其使用壽命是普通高錳鋼的2-4倍。
序號(hào) |
牌號(hào) |
化學(xué)成份Chemical Compostion(%) |
||||||||
C |
Si |
Mn |
Cr |
Mo |
Ni |
Cu |
S |
P |
||
1 |
ZG30Gr5MoMnRe |
0.25-0.35 |
0.3-1.0 |
0.3-1.0 |
4.5-5.5 |
0.7-1.0 |
|
|
≤0.045 |
≤0.0045 |
2 |
ZG40Gr5MoMnRe |
0.35-0.45 |
0.3-1.0 |
0.3-1.0 |
4.5-5.5 |
0.7-1.0 |
|
|
≤0.045 |
≤0.045 |
3 |
ZG45Cr3NiMoMnRe |
0.40-0.50 |
0.3-0.8 |
0.6-1.2 |
2.0-3.2 |
0.3-0.5 |
0.5-1.0 |
|
≤0.04 |
≤0.04 |
4 |
ZG90Cr6MoMn |
0.85-0.95 |
0.4-0.8 |
0.3-0.8 |
5-8 |
0.2-0.4 |
|
|
≤0.04 |
≤0.04 |
5 |
ZGMn13 |
1.1-1.4 |
0.3-1.0 |
11-14 |
|
|
|
|
≤0.06 |
≤0.09 |
6 |
ZGMn13Cr2 |
1.1-1.4 |
0.3-1.0 |
11-14 |
1.5-2.5 |
0-0.5 |
|
|
≤0.06 |
≤0.08 |
7 |
ZGMn17Cr2 |
1.1-1.4 |
0.3-1.0 |
16-19 |
10-2.0 |
|
Ti0.2-0.4 |
|
≤0.06 |
≤0.08 |
8 |
ZG20Cr26Ni5 |
≤0.20 |
≤2.0 |
≤2.0 |
22-26 |
≤0.50 |
4-6 |
|
≤0.04 |
≤0.04 |
9 |
ZG35Cr26Ni12 |
0.2-0.5 |
≤2.0 |
≤2.0 |
22-26 |
≤0.50 |
11-14 |
|
≤0.04 |
≤0.04 |
10 |
ZG40Cr26Ni20 |
0.35-0.45 |
≤2.0 |
≤2.0 |
23-27 |
≤0.50 |
19-22 |
|
≤0.04 |
≤0.04 |
11 |
KmTBCr15Mo2 |
2-2.8 |
≤1.0 |
0.5-1.0 |
12-18 |
0.5-2.5 |
0-1.0 |
0-1.2 |
≤0.06 |
≤0.10 |
12 |
KmTBCr20Mo2 |
2-3.0 |
≤1.0 |
0.5-1.0 |
18-22 |
1.5-2.5 |
0-1.5 |
0.8-1.2 |
≤0.06 |
≤0.10 |
13 |
KmTBCr26 |
2-3.0 |
≤1.0 |
0.5-1.0 |
22-28 |
0-1.0 |
0-1.5 |
0-2.0 |
≤0.06 |
≤0.10 |
序號(hào) |
牌號(hào) |
機(jī)械性能 |
金相組織 |
||
Ak/cm2 |
HRC |
abMpa |
|||
1 |
ZG30Gr5MoMnRe |
≥25 |
≥45 |
|
M+B+C |
2 |
ZG40Gr5MoMnRe |
≥20 |
≥48 |
|
M+B+C |
3 |
ZG45Cr3NiMoMnRe |
≥20 |
≥50 |
|
M+C |
4 |
ZG90Cr6MoMn |
≥7 |
≥50 |
|
M+C |
5 |
ZGMn13 |
≥147 |
HB≤229 |
637 |
A+C |
6 |
ZGMn13Cr2 |
≥80 |
|
|
A+C |
7 |
ZGMn17Cr2 |
≥50 |
|
|
A+C |
8 |
ZG20Cr26Ni5 |
|
|
590 |
A+F |
9 |
ZG35Cr26Ni12 |
|
|
490 |
A+F |
10 |
ZG40Cr26Ni20 |
|
|
440 |
A+F |
11 |
KmTBCr15Mo2 |
|
≥53 |
|
M+A+C |
12 |
KmTBCr20Mo2 |
≥3 |
≥58 |
|
M+A+C |
13 |
KmTBCr26 |
|
≥52 |
|
M+A+C |